Ce微合金化对取向硅钢高温退火组织和织构的影响

文档摘要：利用金相显微镜观察晶粒尺寸的变化,利用X射线衍射(XRD),测定实验钢的宏观织构,分析织构类型及变化规律.实验结果表明:在高温退火时,随着退火温度的升高,晶粒尺寸呈先增大后减小的趋势,Ce有利于高温退火过程中形成尺寸较大的晶粒.高温退火温度为1210℃时晶粒尺寸最大,含Ce(1#)实验钢平均尺寸在2.21mm,局部有3.25mm的大晶粒出现,不含Ce(2#)实验钢平均晶粒尺寸为1.22mm.添加Ce有利于高温退火后高斯织构的形成,选取织构密度范围(2,4,6,8,10)时含Ce(1#)实验钢高斯织构密度10.1在φ1方向偏离约5°,不含Ce(2#)实验钢高斯织构密度8.0在φ1偏离约20°.

Abstract：TheeffectofCeonthemicrostructuresandmicrostructuresof3%Si-orientedsiliconsteelafterhigh-temperatureannealingwasstudiedbyusingatubefurnaceinthesimulatedannealingprocess.Thegrainsizewasobservedbymetallographicmicroscope.X-raydiffraction(XRD)wasusedtodeterminethemacroscopictextureofthesamples,andthetypesoftexturesandthevariationlawswereanalyzed.Theexperimentalresultsshowthatthegrainsizefirstincreasesandthendecreaseswithincreasingtheannealingtemperature,andCeisfavorablefortheformationoflargesizegrainsduringhightemperatureannealing,withthelargestgrainsizeobtainedatannealingtemperatureof1210℃.TheaveragegrainsizeofCe(1#)teststeelis2.21mm,thelocalgrainsizeis3.25mm,andtheaveragegrainsizeof2#teststeelwithoutCeis1.22mm.TheGaussiantexturedensityofCe(1#)teststeelintherangeoftexturedensity(2,4,6,8,10)isabout5°inφ1direction,andtheGaussiantexturedensity(8.0)intheabsenceofCe(2#)isabout20°fromφ1.

作者：杨劼  任慧平  金自力  李东岳  王朝毅Author：YANGJie  RENHui-ping  JINZi-li  LIDong-yue  WANGZhao-yi
作者单位：内蒙古科技大学材料与冶金学院,内蒙古包头,014010
刊名：内蒙古科技大学学报
Journal：JournalofInnerMongoliaUniversityofScienceandTechnology
年，卷(期)：2017, 36(1)
分类号：TF801
关键词：抑制剂  高温退火  取向硅钢  Ce  
Keywords：Inhibitor  hightemperatureannealing  orientedsiliconsteel  Ce  
机标分类号：
在线出版日期：2017年5月31日
基金项目：Ce微合金化对取向硅钢高温退火组织和织构的影响[
期刊论文]  内蒙古科技大学学报--2017, 36(1)杨劼  任慧平  金自力  李东岳  王朝毅利用金相显微镜观察晶粒尺寸的变化,利用X射线衍射(XRD),测定实验钢的宏观织构,分析织构类型及变化规律.实验结果表明:在高温退火时,随着退火温度的升高,晶粒尺寸呈先增大后减小的趋势,Ce有利于高温退火过程中形成尺寸较...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文

关键词：抑制剂,高温退火,取向硅钢,Ce,

2024-10-3 23:13 上传 Ce微合金化对取向硅钢高温退火组织和织构的影响.pdf

文件大小:

636.4 KB

下载次数:

60

高速下载