文档名：钛酸锂电池常温循环寿命研究
摘要：钛酸锂电池的循环寿命是其一项重要性能评价指标.文中以软包钛酸锂电池为研究对象,在常温下开展循环老化试验,通过电压微分分析和容量增量分析等原位分析方法对电池全生命周期内的容量衰减、内阻增加等原因进行分析,提出了一种基于特征参数的剩余容量估计方法.经综合分析得到:钛酸锂电池容量衰退的主要原因是正极材料损失和锂离子损失,而电池在寿命末期容量加速衰退的原因是电池内阻急剧增大.
Abstract：Thecyclelifeoflithiumtitanatebatteryisanimportantperformanceevaluationindex.Inthispaper,thesoftcoatedlithiumtitanatebatteryistakenastheresearchobject,andthecyclicagingtestiscarriedoutatroomtemperature.Thecausesofcapacityattenuationandinternalresistanceincreaseinthewholelifecycleofthebatteryareanalyzedthroughthein-situanalysismethodssuchasvoltagedifferentialanalysisandcapacityincrementanalysis,andaresidualcapacityestimationmethodbasedoncharacteristicparametersisproposed.Accordingtothecomprehensiveanalysis,themainreasonsforthecapacitydeclineoflithiumtitanatebatteryarethelossofcathodematerialsandlithiumion,whilethereasonfortheacceleratedcapacitydeclineattheendofthebatterylifeisthesharpincreaseoftheinternalresistanceofthebattery.
作者：姚正斌 陈浩泽 黄健 姜君 Author：YaoZhengbin ChenHaoze HuangJian JiangJun
作者单位：中车青岛四方机车车辆股份有限公司技术中心,山东青岛266111北京交通大学国家能源主动配电网技术研发中心,北京100044中国铁道科学研究院集团有限公司标准计量研究所,北京100081
刊名：电测与仪表 ISTICPKU
Journal：ElectricalMeasurement&Instrumentation
年，卷(期)：2023, 60(11)
分类号：TM911
关键词：钛酸锂电池 循环寿命 衰退机理
Keywords：lithiumtitanatebattery cyclelife agingmechanism
机标分类号：TM912.4TQ028.8TN301
在线出版日期：2023年12月26日
基金项目：国家重点研发计划钛酸锂电池常温循环寿命研究[
期刊论文] 电测与仪表--2023, 60(11)姚正斌 陈浩泽 黄健 姜君钛酸锂电池的循环寿命是其一项重要性能评价指标.文中以软包钛酸锂电池为研究对象,在常温下开展循环老化试验,通过电压微分分析和容量增量分析等原位分析方法对电池全生命周期内的容量衰减、内阻增加等原因进行分析,提出...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
钛酸锂电池常温循环寿命研究 Research on cycle life of lithium titanate battery at room temperature
钛酸锂电池常温循环寿命研究.pdf
- 文件大小:
- 7.64 MB
- 下载次数:
- 60
-
高速下载
|
|