文档名：2,3吡啶二羧酸酐用于高电压锂离子电池电解液
摘要：将2,3-吡啶二羧酸酐(PDA)作为功能型添加剂加入电解液中,可拓宽电解液的氧化还原窗口,并先于溶剂在正负极表面形成保护膜.添加2.0%PDA后,钴酸锂/石墨全电池在85℃下存储18h,厚度膨胀率从37.0%降低至8.4%;45℃下,以1.0C在3.0～4.5V循环600次,容量保持率从58.3%提升至84.9%;在45℃浮充测试中,含2.0%添加剂的电池78d后厚度膨胀率仅为9.7%.过多的PDA会导致负极阻抗显著增加,出现析锂现象.综合考虑常温和高温性能,PDA添加质量分数建议为1.0%.
Abstract：2,3-pyridinedicarboxylicanhydride(PDA)wasappliedasafunctionaladditiveintheelectrolyte.Theoxidation-reductionwindowofelectrolytecouldbeexpanded,PDAwouldpreferentiallyformaprotectivefilmonthesurfaceofcathodeandanode.Adding2.0%PDAadditivetotheelectrolyte,thethicknessswellingrateoftheLiCoO2/graphitefullbatterydecreasedfrom37.0%to8.4%after85℃storagefor18h,thecapacityretentionincreasedfrom58.3%to84.9%aftercycle600timesat1.0Cin3.0-4.5Vat45℃.Inthe45℃floatingchargetest,thethicknessswellingrateofbatterywith2.0%PDAwasonly9.7%after78d.ToomuchPDAledtoasignificantincreaseinanodeimpedanceandlithiumprecipitation.ItwasrecommendedthatthemassfractionofPDAadditionshouldbe1.0%bycomprehensivelyconsideringtheperformanceatroomtemperatureandhightemperature.
作者：胡大林 李枫 张方畅 卢周广 Author：HUDa-lin LIFeng ZHANGFang-chang LUZhou-guang
作者单位：深圳市豪鹏科技股份有限公司,广东深圳518111;南科大材料系-豪鹏科技新能源联合实验室,广东深圳518055南方科技大学材料科学与工程系,深圳市界面材料界面科学与工程应用重点实验室,广东深圳518055;南科大材料系-豪鹏科技新能源联合实验室,广东深圳518055
刊名：电池 ISTICPKU
Journal：BatteryBimonthly
年，卷(期)：2023, 53(6)
分类号：TM912.9
关键词：电解液 添加剂 高电压 钴酸锂(LiCoO2) 2,3-吡啶二羧酸酐(PDA) 高温性能 锂离子电池
Keywords：electrolyte additive highvoltage lithiumcobaltoxide(LiCoO2) 2,3-pyridinedicarboxylicanhydride(PDA) hightemperatureperformance Li-ionbattery
机标分类号：O646TM912.9TM836
在线出版日期：2024年1月10日
基金项目：国家自然科学基金，深圳市基础研究重点项目2,3-吡啶二羧酸酐用于高电压锂离子电池电解液[
期刊论文] 电池--2023, 53(6)胡大林 李枫 张方畅 卢周广将2,3-吡啶二羧酸酐(PDA)作为功能型添加剂加入电解液中,可拓宽电解液的氧化还原窗口,并先于溶剂在正负极表面形成保护膜.添加2.0%PDA后,钴酸锂/石墨全电池在85℃下存储18h,厚度膨胀率从37.0%降低至8.4%;45℃下,以...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
2,3-吡啶二羧酸酐用于高电压锂离子电池电解液 Application of 2,3-pyridinedicarboxylic anhydride in electrolyte of high voltage Li-ion battery
2,3-吡啶二羧酸酐用于高电压锂离子电池电解液.pdf
- 文件大小:
- 2.87 MB
- 下载次数:
- 60
-
高速下载
|
|