摘要：[目的]化学抛光是高温合金化学铣切的关键步骤之一,能够去除高温合金表面的微观不平整缺陷,令其满足航空航天、石油化工等领域对零件表面高品质的要求.[方法]通过正交试验和单因素实验研究了抛光液配方和工艺参数对GH625高温合金化学抛光速率和表面粗糙度的影响.[结果]GH625高温合金化学抛光的较佳配方和工艺条件为:盐酸100g/L,硝酸170g/L,氢氟酸90g/L,Fe3+170g/L,温度50℃,时间5min,试片水平放置.在该条件下化学抛光后,GH625高温合金表面变得平整均匀而富有金属光泽,表面粗糙度Ra从初始的10.3μm降至1.1μm.[结论]本文的研究结果可为GH625高温合金的化学抛光提供参考.
Abstract：[Introduction]Chemicalpolishingisoneofthekeystepsinchemicalmillingofsuperalloys,whichcanremovemicroscopicallyunevendefectsontheirsurfaces,enablingthesuperalloystomeetthehigh-qualitysurfacerequirementsofaerospace,petrochemical,andotherfields.[Method]TheeffectsofthecompositionofpolishingsolutionandprocessparametersonthematerialremovalrateandsurfaceroughnessofGH625superalloywerestudiedbyorthogonaltestandsingle-factorexperiments.[Result]ThecompositionofpolishingsolutionandprocessparametersforchemicalpolishingofGH625superalloywereoptimizedasfollows:chlorideacid100g/L,nitricacid170g/L,hydrofluoricacid90g/L,Fe3+170g/L,temperature50℃,time5min,andhorizontalplacementofspecimensinpolishingsolution.Afterbeingchemicallypolishedundertheoptimizedconditions,thesurfaceofGH625superalloybecamesmooth,uniform,andbright,anditssurfaceroughnessRawasdecreasedfrom10.3μminitiallyto1.1μm.[Conclusion]ThisresearchprovidesareferenceforchemicalpolishingofGH625superalloy.
作者：马宁 张峻山Author：MANing ZHANGJunshan
作者单位：沈阳航空航天大学机电工程学院,辽宁沈阳110136
刊名：电镀与涂饰
Journal：Electroplating&Finishing
年，卷(期)：2024, 43(4)
分类号：TG175
关键词：镍基高温合金 化学抛光 表面粗糙度 材料去除速率
Keywords：nickel-basedsuperalloy chemicalpolishing surfaceroughness materialremovalrate
机标分类号：TG132.3TG407TG506
在线出版日期：2024年5月11日
基金项目：GH625镍基高温合金化学抛光工艺[
期刊论文] 电镀与涂饰--2024, 43(4)马宁 张峻山[目的]化学抛光是高温合金化学铣切的关键步骤之一,能够去除高温合金表面的微观不平整缺陷,令其满足航空航天、石油化工等领域对零件表面高品质的要求.[方法]通过正交试验和单因素实验研究了抛光液配方和工艺参数对GH625...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
GH625镍基高温合金化学抛光工艺 Chemical polishing of GH625 nickel-based superalloy
GH625镍基高温合金化学抛光工艺.pdf
- 文件大小:
- 1.01 MB
- 下载次数:
- 60
-
高速下载
|