钙钛矿结构Li0.33La0.557Ti0.7Cr0.3O3包覆稳定富锂锰基正极

文档名：钙钛矿结构Li0.33La0.557Ti0.7Cr0.3O3包覆稳定富锂锰基正极
摘要：富锂锰基层状氧化物凭借超高的放电比容量和较低的价格成为了极具发展前景的锂离子电池正极材料,然而,首次库仑效率较低、容量衰减严重以及较差的倍率性能等缺点制约了其进一步的应用.选用离子-电子混合导体Li0.33La0.557Ti0.7Cr0.3O3作为包覆层材料,并采用共沉淀法和高温退火法将其包覆于正极颗粒上.包覆量为2%的样品性能最佳,在0.5C下、2.0～4.8V电压范围内,200次循环容量保持率可以达到88.2%,相比于原始样品的62.1%有了明显的提升.

Abstract：Lithium-richmanganese-basedoxideshavebecomearesearchhotspotduetotheirultra-highdischargespecificcapacityandlowprice,andtheyarepromisingcathodematerialsforlithiumionbatteries.However,thedisadvantagesoflowfirstcoulombicefficiency,severecapacityfading,andpoorrateperformancerestrictitsfurtherapplications.Inthispaper,theion-electronmixedcon-ductorLi0.33La0.557Ti0.7Cr0.3O3wasselectedasthecoatingmaterial,andwascoatedonthepositiveelec-trodeparticlesbyco-precipitationandhightemperatureannealing.Thesamplewithacoatingamountof2%hasthebestperformance.Atthecurrentrateof0.5Candthevoltagerangeof2.0～4.8V,thecapacityretentionrateafter200cyclescanreach88.2%,whichisasignificantimprovementcomparedwith62.1%ofthepristinesample.

作者：刘磊磊  薛文东  黄冰心Author：LIULeilei  XUEWendong  HUANGBingxin
作者单位：北京科技大学顺德创新学院,广东佛山528399
刊名：电源技术
Journal：ChineseJournalofPowerSources
年，卷(期)：2024, 48(1)
分类号：TM912
关键词：锂离子电池  富锂锰基正极  表面包覆  循环性能  
Keywords：Li-ionbattery  Li-richMn-basedcathode  surfacecoating  cyclestability  
机标分类号：TM282TM912.9TB383
在线出版日期：2024年3月5日
基金项目：科技部重点研发项目，佛山市科技创新基金，佛山市科技创新基金，佛山市科技创新基金钙钛矿结构Li0.33La0.557Ti0.7Cr0.3O3包覆稳定富锂锰基正极[
期刊论文]  电源技术--2024, 48(1)刘磊磊  薛文东  黄冰心富锂锰基层状氧化物凭借超高的放电比容量和较低的价格成为了极具发展前景的锂离子电池正极材料,然而,首次库仑效率较低、容量衰减严重以及较差的倍率性能等缺点制约了其进一步的应用.选用离子-电子混合导体Li0.33La0.55...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文

        钙钛矿结构Li0.33La0.557Ti0.7Cr0.3O3包覆稳定富锂锰基正极  Perovskite structure Li0.33La0.557Ti0.7Cr0.3O3 coated stable Li-rich Mn-based cathode

钙钛矿结构Li0.33La0.557Ti0.7Cr0.3O3包覆稳定富锂锰基正极.pdf

2024-12-14 13:34 上传 钙钛矿结构Li0.33La0.557Ti0.7Cr0.3O3包覆稳定富锂锰基正极.pdf

文件大小:

1.05 MB

下载次数:

60

高速下载