文档名：高流动抗冲聚丙烯EP533N质量优化
摘要：根据高流动抗冲共聚聚丙烯EP533N市场质量反馈信息,采取使用新型催化剂-给电子体体系,优化聚合、汽蒸、干燥、挤压等单元的工艺参数,优选复合助剂体系等措施提升产品质量.结果表明,采用新型催化剂体系,工艺参数优化为:流化床反应器中乙烯与乙烯和丙烯混合气的摩尔比降至0.33～0.36,气相反应器内温度升至79～81℃,汽蒸器中蒸汽量升至2000～2200kg/h,挤压机筒体温度降至200～210℃.优化后,EP533N的弯曲模量达到1327MPa,冲击强度稳定在9.50kJ/m2以上,气味等级降至2.85级;产品质量优于市场同类产品,满足市场需求.
Abstract：BasedonthemarketfeedbackinformationofhighflowandimpactcopolymerizedpolypropyleneEP533N,anewcatalyst-electrondonorsystemwasusedtooptimizetheprocessparametersofpolymerization,steaming,drying,extrusionandotherunits,andtooptimizethecompositeadditivesystemtoimproveproductquality.Theresultsshowthattheoptimizedparametersoftheprocessadoptednewcatalystsystemareasfollows:theethylenegasratiointhefluidizedbedreactorisreducedto0.33-0.36,thetemperatureinthefluidizedreactorisincreasedto79-81℃,thesteamvolumeintheevaporatorisincreasedto2000-2200kg/h,andthetemperatureoftheextrudercylinderisreducedto200-210℃.ThebendingmodulusofEP533Nreaches1327MPa,itsimpactstrengthremainsstableat9.50kJ/m2,anditsodorlevelisreducedto2.85levelafteroptimization.Theproductqualityissuperiortothatofsimilarproductsinthemarket,meetingmarketdemand.
作者：孙建敏 樊晓睿 Author：SunJianmin FanXiaorui
作者单位：中国石油天然气股份有限公司兰州石化分公司乙烯厂,甘肃兰州730060北京化工大学材料科学与工程学院,北京102200
刊名：合成树脂及塑料 ISTICPKU
Journal：ChinaSyntheticResinandPlastics
年，卷(期)：2024, 41(3)
分类号：TQ325.1+4
关键词：抗冲共聚聚丙烯 弯曲模量 气味 收缩率
Keywords：impactcopolymerizedpolypropylene bendingmodulus odor shrinkagerate
机标分类号：TQ325.14TQ052.5TN929.5
在线出版日期：2024年6月19日
基金项目：高流动抗冲聚丙烯EP533N质量优化[
期刊论文] 合成树脂及塑料--2024, 41(3)孙建敏 樊晓睿根据高流动抗冲共聚聚丙烯EP533N市场质量反馈信息,采取使用新型催化剂-给电子体体系,优化聚合、汽蒸、干燥、挤压等单元的工艺参数,优选复合助剂体系等措施提升产品质量.结果表明,采用新型催化剂体系,工艺参数优化为:流化...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
高流动抗冲聚丙烯EP533N质量优化 Quality optimization of high flow and impact polypropylene EP533N
高流动抗冲聚丙烯EP533N质量优化.pdf
- 文件大小:
- 680.61 KB
- 下载次数:
- 60
-
高速下载
|