文档名：海洋环境下钢结构用水性无机富锌底漆的制备及性能
摘要：[目的]海洋钢结构长时间暴露在高盐雾、高湿热、阳光曝晒等环境下会发生严重的腐蚀,而目前大多数水性无机富锌底漆含锌量大、成本高.[方法]采用自制高模数硅酸钾溶液作为基料,通过优化制备条件,获得了一种贮存稳定性高、耐腐蚀性能强、干燥时间短的水性无机富锌底漆.[结果]当采用季铵类稳定剂来制备硅酸钾溶液,增稠剂用量为8.6%(质量分数)时,得到的基料可在50℃下稳定贮存30d.以基料与锌粉的质量比1.0∶1.2制备的涂层抵御中性盐雾腐蚀的时间长达5000h.[结论]该底漆可用于海洋环境下的钢结构防腐.
Abstract：[Introduction]Marinesteelstructuressufferfromseverecorrosionduetothelong-termexposuretohighsaltspray,highhumidity,andsunlight.Currently,mostwater-basedinorganiczinc-richprimershavehighzinccontentandhighcost.[Method]Awater-basedinorganiczinc-richprimerwithgoodstoragestability,strongcorrosionresistance,andshortdryingtimewasobtainedbyusingahome-madehigh-moduluspotassiumsilicatesolutionasthebinderafteroptimizingthepreparationconditions.[Result]Thebinderpreparedfromthepotassiumsilicatesolutionstabilizedbyusingaquaternaryammoniumcompoundwith8.6%(massfraction)ofthickenercouldbestablystoredat50℃for30days.Thecoatingpreparedwithamassratioofbindertozincpowder1.0:1.2couldendureupto5000hoursofneutralsaltspraycorrosion.[Conclusion]Thisprimercanbeusedforanticorrosionofsteelstructuresinmarineenvironment.
作者：李伟铭 郭占魁 王敬伟 Author：LIWeiming GUOZhankui WANGJingwei
作者单位：东营市赫邦化工有限公司,山东东营257237山东龙港硅业科技有限公司,山东昌邑261300
刊名：电镀与涂饰
Journal：Electroplating&Finishing
年，卷(期)：2024, 43(4)
分类号：TU56+1.67
关键词：钢结构 水性无机富锌底漆 海洋环境 贮存稳定性 耐腐蚀
Keywords：steelstructure water-basedinorganiczinc-richprimer marineenvironment storagestability anticorrosion
机标分类号：TG178TQ630.7TU366.1
在线出版日期：2024年5月11日
基金项目：潍坊市科学技术发展计划项目海洋环境下钢结构用水性无机富锌底漆的制备及性能[
期刊论文] 电镀与涂饰--2024, 43(4)李伟铭 郭占魁 王敬伟[目的]海洋钢结构长时间暴露在高盐雾、高湿热、阳光曝晒等环境下会发生严重的腐蚀,而目前大多数水性无机富锌底漆含锌量大、成本高.[方法]采用自制高模数硅酸钾溶液作为基料,通过优化制备条件,获得了一种贮存稳定性高、耐腐...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
海洋环境下钢结构用水性无机富锌底漆的制备及性能 Preparation and properties of a water-based inorganic zinc-rich primer for steel structures in marine environment
海洋环境下钢结构用水性无机富锌底漆的制备及性能.pdf
- 文件大小:
- 672.96 KB
- 下载次数:
- 60
-
高速下载
|