文档名：镀钛对2195铝锂合金耐磨和腐蚀性能的影响
摘要：通过摩擦磨损试验和电化学工作站等测试,研究了2195-T6铝锂合金表面镀钛处理前后的摩擦磨损性能和电化学性能,探讨了浸泡实验的腐蚀机制.结果表明:镀钛后铝锂合金表层的纳米压痕硬度略有提高,表层晶粒得到了细化;镀钛前后的摩擦系数基本相同,磨损性能得到了提高;镀钛后铝锂合金的腐蚀电位提高,腐蚀电流密度减小,阻抗谱半径变大.3.5%NaCl溶液中的浸泡实验显示,镀钛试样的点腐蚀明显改善,这是由于合金表面形成的钛膜起到了隔离保护作用.
Abstract：Thewearandelectrochemicalpropertiesof2195-T6Al-Lialloybeforeandaftertitaniumplatingwereinvestigatedbyfriction-weartestandelectrochemicalmeasurement,respectively.Thecorrosionmechanismofimmersionexperimentwasdiscussed.TheresultsindicatethatthesurfacenanoindentationhardnessofAl-Lialloyslightlyincreasesandthesurfacegrainsarerefinedaftertitani-umplating.Thefrictioncoefficientsarebasicallythesamebeforeandaftertitaniumplating,andthewearperformanceisimproved.ThecorrosionpotentialofAl-Lialloyincreases,thecorrosioncurrentdensityreduces,andtheimpedancespectrumradiusenlargesaftertitaniumplating.Thisisbecausethetitaniumfilmformedonthealloyplaystherolesofisolationandprotection.
作者：苏海 张殿喜 窦忠宇 陈召松 吴明华 Author：SuHai ZhangDianxi DouZhongyu ChenZhaosong WuMinghua
作者单位：安顺学院电子与信息工程学院,贵州安顺561000;贵州安大航空锻造有限责任公司,贵州安顺561000安顺学院电子与信息工程学院,贵州安顺561000
刊名：电镀与精饰 ISTICPKU
Journal：Plating&Finishing
年，卷(期)：2024, 46(5)
分类号：TG174
关键词：铝锂合金 镀钛 摩擦磨损 腐蚀性能
Keywords：aluminumlithiumalloy platingtitanium frictionandwear corrosionperformance
机标分类号：TG146.2TG453TG249
在线出版日期：2024年5月16日
基金项目：合作协同育人项目镀钛对2195铝锂合金耐磨和腐蚀性能的影响[
期刊论文] 电镀与精饰--2024, 46(5)苏海 张殿喜 窦忠宇 陈召松 吴明华通过摩擦磨损试验和电化学工作站等测试,研究了2195-T6铝锂合金表面镀钛处理前后的摩擦磨损性能和电化学性能,探讨了浸泡实验的腐蚀机制.结果表明:镀钛后铝锂合金表层的纳米压痕硬度略有提高,表层晶粒得到了细化;镀钛前...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
镀钛对2195铝锂合金耐磨和腐蚀性能的影响 Effect of titanium plating on wear resistance and corrosion properties of 2195 Al-Li alloy
镀钛对2195铝锂合金耐磨和腐蚀性能的影响.pdf
- 文件大小:
- 1.46 MB
- 下载次数:
- 60
-
高速下载
|