文档名：航天用高强度弹簧镀锌工艺替代方案研究
摘要：[目的]高强度弹簧是常用于为导弹空气舵、弹翼展开锁定提供驱动力的零件,通常采用高强度钢制造,以镀锌作为其表面防护手段,但该工艺过程存在氢脆导致弹簧脆性断裂的风险.[方法]分别对高强钢进行镀锌、镀锌镍合金、达克罗涂覆和离子镀铝,对比了不同镀(涂)层的厚度、结合力和耐蚀性,以寻找镀锌替代方案.[结果]达克罗涂覆、离子镀铝和镀锌镍合金都属于无氢脆或低氢脆表面处理工艺,但更推荐采用镀锌镍合金代替高强钢镀锌工艺.[结论]选择合适的表面处理工艺能够在一定程度上避免高强钢弹簧氢脆断裂问题.
Abstract：[Introduction]High-strengthspringsarecommonlyusedasthecomponentstoprovidedrivingforcefordeploymentandlockingofmissileairruddersandwings.Thesespringsareusuallymadeofhigh-strengthsteelandtreatedbyzincplatingtoofferasurfaceprotection,butthereisariskofbrittlefracturecausedbyhydrogenembrittlementduringthezincplatingprocess.[Method]Thehigh-strengthsteelwastreatedbyzincplating,zinc-nickelplating,Dacrometcoating,andaluminumionplating,respectively.Thethickness,adhesion,andcorrosionresistanceofthefourkindsofcoatingswerecomparedtofindoutasuitablealternativetozincplating.[Result]Thehigh-strengthsteelstreatedbyDacrometcoating,aluminumionplating,orzinc-nickelalloyplatinghaslittleornohydrogenembrittlement,butzinc-nickelalloyplatingismorerecommendedforreplacingthezincplating.[Conclusion]Thebrittlefractureofhigh-strengthspringcausedbyhydrogenembrittlementcanbesolvedbyselectingasurfacetreatmenttechnologyproperly.
作者：魏建中 王福光 郭文营 Author：WEIJianzhong WANGFuguang GUOWenying
作者单位：北京新风航天装备有限公司,北京100854航天科工防御技术研究试验中心,北京100854
刊名：电镀与涂饰
Journal：Electroplating&Finishing
年，卷(期)：2024, 43(2)
分类号：TG178
关键词：航天 弹簧 镀锌 锌镍合金 达克罗涂层 离子镀铝 氢脆 耐蚀性
Keywords：aerospace spring zincplating zinc-nickelalloy Dacrometcoating aluminumionplating hydrogenembrittlement corrosionresistance
机标分类号：TG146.1TQ153.2TG457.11
在线出版日期：2024年3月22日
基金项目：航天用高强度弹簧镀锌工艺替代方案研究[
期刊论文] 电镀与涂饰--2024, 43(2)魏建中 王福光 郭文营[目的]高强度弹簧是常用于为导弹空气舵、弹翼展开锁定提供驱动力的零件,通常采用高强度钢制造,以镀锌作为其表面防护手段,但该工艺过程存在氢脆导致弹簧脆性断裂的风险.[方法]分别对高强钢进行镀锌、镀锌镍合金、达克罗涂...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
航天用高强度弹簧镀锌工艺替代方案研究 Study on substitute for zinc plating on aerospace high-strength spring
航天用高强度弹簧镀锌工艺替代方案研究.pdf
- 文件大小:
- 3.06 MB
- 下载次数:
- 60
-
高速下载
|