文档名：拟薄水铝石制备条件对其表面羟基性质的影响
摘要：采用连续法制备拟薄水铝石,考察拟薄水铝石制备条件对其表面羟基性质的影响,并采用红外光谱等分析样品的表面羟基类型及含量.结果表明,合成条件对羟基的比例影响较大,尤其是Ⅲ型羟基(中性)的范围变化较大,最高为N-4样品的94.61％,最低为N-16样品的31.84％.羟基峰面积的改变导致羟基峰的位置也发生了不同程度的偏移,且基本表现为3680cm-1峰位和/或3730cm-1峰位减小,3730cm-1峰位和/或3790cm-1峰位增加的趋势.
Abstract：Acontinuousmethodwasusedtopreparepseudoboehmite,andcorrespondingorthogonalexperimentsweredesignedtoinvestigatetheeffectofpreparationconditionsonthesurfacehydroxylprop-ertiesofpseudoboehmite.Thetypesandcontentsofsurfacehydroxylgroupsintheobtainedsampleswereanalyzedbyinfraredspectroscopyandothermethods.Theresultsshowthatthesynthesisconditionshaveasignificantimpactontheproportionofhydroxylgroups,especiallytherangeoftypeⅢhydroxylgroups(neutral)withthehighestvalue94.61％ofN-4andthelowest31.84％ofN-16.Thechangeinhydroxylpeakarealeadstovaryingdegreesofshiftinthepositionofthehydroxylpeak,whichisgenerallymanifestedasadecreaseinthe3680cm-1peakand/or3730cm-1peak,andanincreaseinthe3730cm-1peakand/or3790cm-1peak.
作者：刘文洁 穆福军 隋宝宽 袁胜华Author：LiuWenjie MuFujun SuiBaokuan YuanShenghua
作者单位：中石化(大连)石油化工研究院有限公司,辽宁大连116045
刊名：工业催化 ISTIC
Journal：IndustrialCatalysis
年，卷(期)：2024, 32(6)
分类号：TQ426.6O643.36
关键词：催化剂工程 连续法 制备条件 拟薄水铝石 表面羟基
Keywords：catalystengineering continuousmethod preparationconditions pseudo-boehmite surfacehydroxylgroup
机标分类号：O6TQ115V512
在线出版日期：2024年7月8日
基金项目：中国石化重点科技项目拟薄水铝石制备条件对其表面羟基性质的影响[
期刊论文] 工业催化--2024, 32(6)刘文洁 穆福军 隋宝宽 袁胜华采用连续法制备拟薄水铝石,考察拟薄水铝石制备条件对其表面羟基性质的影响,并采用红外光谱等分析样品的表面羟基类型及含量.结果表明,合成条件对羟基的比例影响较大,尤其是Ⅲ型羟基(中性)的范围变化较大,最高为N-4样品的...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
拟薄水铝石制备条件对其表面羟基性质的影响 The influence of preparation conditions on the surface hydroxyl properties of pseudo boehmite
拟薄水铝石制备条件对其表面羟基性质的影响.pdf
- 文件大小:
- 10.17 MB
- 下载次数:
- 60
-
高速下载
|