文档名：类金刚石膜层制备及摩擦磨损性能
摘要：为解决某型扭力臂轴及配合衬套的磨损问题,使用磁控溅射和等离子增强化学气相沉积技术,在30CrMnSi-Ni2A表面制备了渐变过渡结构的类金刚石膜层(DLC).使用球磨法、纳米压痕法、划痕法测量DLC膜层性能,膜厚为4.3μm,硬度≥1900HV,膜基结合力≥30N.经过滑动磨损测试,膜层摩擦系数≤0.2,摩擦磨损率≤2×10-6mm3·r-1.经过20000转次耐磨测试,与硬铬镀层的扭力臂轴对比,DLC膜层配合衬套的磨损量远低于硬铬镀层配合衬套,可满足扭力臂轴耐磨润滑需求.
Abstract：Tosolvethewearproblemoftorsionarmshaftandsleeve,diamond-likecarbonfilm(DLC)withagradualtransitionstructurewaspreparedonthesurfaceof30CrMnSiNi2Ausingmagnetronsputteringandplasmaenhancedchemicalvapordepositiontechnology.TheperformanceofDLCfilmwasmeasuredusingballmilling,nano-indentationandscratchmethods,withafilmthicknessof4.3μm.Thehardnesswashigherthan1900HV,andthebindingforcebetweenthefilmandsubstratewashigherthan30N.Byslidingweartest,thefrictioncoefficientofthefilmwaslessthan0.2,andthefrictionandwearratewaslessthan2×10-6mm3·r-1.Through20000revolutionsofwearresistancetesting,comparedwiththetorsionarmshaftofhardchromiumcoating,thewearamountofDLCfilmmatchingsleevewasmuchlowerthanthatofhardchromiumcoatingmatchingsleeve,whichcouldmeetthewearandlubricationrequirementsofthetorquearmshaft.
作者：陈文举 李博 周圣杰 Author：ChenWenju LiBo ZhouShengjie
作者单位：中航飞机起落架有限责任公司,陕西汉中723000成都中云世纪科技有限公司,四川成都610000
刊名：电镀与精饰 ISTICPKU
Journal：Plating&Finishing
年，卷(期)：2024, 46(6)
分类号：TG174.444
关键词：类金刚石膜层 梯度过渡 结合力 耐磨润滑
Keywords：diamond-likecarbonfilm gradienttransition bindingforce wearresistanceandlubrica-tionperformance
机标分类号：TG174.44TB383TH117.3
在线出版日期：2024年6月18日
基金项目：类金刚石膜层制备及摩擦磨损性能[
期刊论文] 电镀与精饰--2024, 46(6)陈文举 李博 周圣杰为解决某型扭力臂轴及配合衬套的磨损问题,使用磁控溅射和等离子增强化学气相沉积技术,在30CrMnSi-Ni2A表面制备了渐变过渡结构的类金刚石膜层(DLC).使用球磨法、纳米压痕法、划痕法测量DLC膜层性能,膜厚为4.3μm,硬度≥19...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
类金刚石膜层制备及摩擦磨损性能 Preparation and friction and wear properties of diamond-like carbon films
类金刚石膜层制备及摩擦磨损性能.pdf
- 文件大小:
- 3.72 MB
- 下载次数:
- 60
-
高速下载
|