文档名：三元动力锂离子电池低温容量失效分析
摘要：为探究动力锂离子电池的低温特性,对比制造工艺相同但低温性能差异较大(A组性能较好)的A、B两组三元动力锂离子电池在低温(-35℃)条件下的容量差异.建立"电池-材料"联动分析方法,从内部材料微观特征分析电池低温容量失效的原因.三元正极材料结构是影响电池低温容量的关键因素.与A组相比,B组电池的正极材料颗粒结构松散,经过低温放电后,颗粒表面出现裂纹,导致B组正极材料在低温放电过程中活性Li+损失、固体电解质相界面(SEI)膜阻抗增加、材料电导率差,继而导致低温容量失效.
Abstract：Inordertoexplorethelow-temperatureperformanceofpowerLi-ionbattery,thecapacitydifferenceoftwogroupsofAandBternarypowerLi-ionbatterieswiththesamemanufacturingprocessbutdifferentlow-temperatureperformance(theperformanceofgroupAisbetter)atlowtemperature(-35℃)iscompared.A"battery-material"linkageanalysismethodisestablishedtoanalyzethecausesoflow-temperaturecapacityfailureofbatteriesfromthemicroscopiccharacteristicsofinternalmaterials.Thestructureofternarycathodematerialisthekeyfactoraffectingthelow-temperaturecapacityofbattery.ComparedwithgroupA,thecathodematerialparticlesofgroupBhavelooserparticle-structure,cracksappearedonthesurfaceoftheparticlesafterdischarge,resultinginthelossofactiveLi+ofthecathodematerialsofgroupBduringthelow-temperaturedischargeprocess,theincreaseofsolidelectrolyteinterface(SEI)filmimpedance,thepoorconductivityofthematerial,whichleadstothefailureoflow-temperaturecapacity.
作者：梁宏毅 黎华玲 甘友毅 邵丹 Author：LIANGHongyi LiHualing GANYouyi SHAODan
作者单位：广汽本田汽车有限公司,广东广州510700广州能源检测研究院,广东省动力电池安全重点实验室,广东广州511447
刊名：电池 ISTICPKU
Journal：BatteryBimonthly
年，卷(期)：2024, 54(2)
分类号：TM912.9
关键词：三元动力锂离子电池 低温 容量 失效
Keywords：ternarypowerLi-ionbattery lowtemperature capacity failure
机标分类号：TM912.9TG111.91TH114
在线出版日期：2024年5月27日
基金项目：国家市场监督管理总局科技计划，广东省市场监督管理局科技项目，广州市科技计划项目，广州市市场监督管理局科技项目三元动力锂离子电池低温容量失效分析[
期刊论文] 电池--2024, 54(2)梁宏毅 黎华玲 甘友毅 邵丹为探究动力锂离子电池的低温特性,对比制造工艺相同但低温性能差异较大(A组性能较好)的A、B两组三元动力锂离子电池在低温(-35℃)条件下的容量差异.建立"电池-材料"联动分析方法,从内部材料微观特征分析电池低温容量失效的...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
三元动力锂离子电池低温容量失效分析 Failure analysis of low-temperature capacity of ternary power Li-ion battery
三元动力锂离子电池低温容量失效分析.pdf
- 文件大小:
- 2.17 MB
- 下载次数:
- 60
-
高速下载
|