文档名：水性有机硅改性环氧树脂的制备与性能
摘要：利用二甲基二氯硅烷(DMDCS)与环氧树脂E51中-OH缩合反应合成有机硅改性环氧树脂,并采用相反转法制备水性有机硅改性环氧树脂,以疏水性优选有机硅改性环氧树脂合成条件,分析了乳化工艺对乳液平均粒径的影响,并考察了固化膜性能.结果表明,在环氧树脂40g、DMDCS1.6g、溶剂用量20mL、50℃反应8h的条件下,有机硅改性环氧树脂与水的接触角为106.8°;当乳化剂用量为25％、乳化温度为65℃、剪切机转速为3000r/min时,乳液平均粒径为1.011μm,储存稳定性(30d)和离心稳定性(3000r/min,30min)良好;水性有机硅改性环氧固化膜固化时间短,具有优良的疏水性、力学性能、耐腐蚀性能.
Abstract：Siliconemodifiedepoxyresinwassynthesizedbythecondensationreactionbetweendichlorodimethylsilane(DMDCS)and-OHofepoxyresinE51,andwaterbornesiliconemodifiedepoxyresinwaspreparedbyreversetransfermethod,andthesynthesisconditionsofsiliconemodi-fiedepoxyresinwereoptimizedbyhydrophobicity.Theinfluenceofemulsificationprocessontheaverageparticlesizeofemulsionwasanalyzed,andthepropertiesofcuredfilmwereinvestigated.Theresultsshowedthatepoxyresin40g,DMDCS1.6g,solventdosage20mL,reactionat50℃for8h,thecontactanglebetweensiliconemodifiedepoxyresinandwaterwas106.8°;emulsifierdosage25％,emulsificationtemperature65℃,shearspeed3000r/min,averageparticlesizeofwaterbornesiliconemodifiedepoxyresinemulsionwas1.011μm,storagestability(30d)andcentrifugalstability(3000r/min,30min)weregood.Waterbornesiliconemodifiedepoxycuringfilmhadshortercuringtime,excel-lenthydrophobicity,mechanicalproperties,corrosionresistance.
作者：何丽红 马悦帆 杨克 徐心硕 李青林 Author：HELihong MAYuefan YANGKe XUXinshuo LIQinglin
作者单位：重庆交通大学材料科学与工程学院,重庆400074重庆交通大学土木工程学院,重庆400074
刊名：材料导报
Journal：MaterialsReports
年，卷(期)：2024, 38(3)
分类号：TQ633
关键词：有机硅改性环氧树脂 水性有机硅改性环氧树脂 疏水性 粒径 固化膜
Keywords：siliconemodifiedepoxyresin waterbornesiliconemodifiedepoxyresin hydrophobicity particlesize curingfilm
机标分类号：TQ323.5TQ423TQ264.1+4
在线出版日期：2024年3月12日
基金项目：水性有机硅改性环氧树脂的制备与性能[
期刊论文] 材料导报--2024, 38(3)何丽红 马悦帆 杨克 徐心硕 李青林利用二甲基二氯硅烷(DMDCS)与环氧树脂E51中-OH缩合反应合成有机硅改性环氧树脂,并采用相反转法制备水性有机硅改性环氧树脂,以疏水性优选有机硅改性环氧树脂合成条件,分析了乳化工艺对乳液平均粒径的影响,并考察了固化...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
水性有机硅改性环氧树脂的制备与性能 Preparation and Properties of Waterborne Silicone Modified Epoxy Resin
水性有机硅改性环氧树脂的制备与性能.pdf
- 文件大小:
- 3.67 MB
- 下载次数:
- 60
-
高速下载
|