文档名：提高120t精炼钢包一次包龄的生产实践
摘要：针对钢包一次包龄低的问题,通过对钢包各部位砖型损毁机理进行分析,提出了一系列改进措施,包括:钢包各部位耐材材质优化;钢包重点部位砌筑防护;使用高性能、长寿命透气砖;优化钢包周转节奏等,并在120t精炼钢包中进行实践验证.结果表明:通过以上改进措施,钢包平均一次包龄由之前的42.35炉提高到62.77炉,最高包龄达到了72炉,耐材和钢包投入成本大幅下降,且对生产组织稳定运行起到了极大的促进作用.
Abstract：Aimingattheissueoflowprimaryladleage,throughanalyzingthemechanismofbricktypedamageinvariouspartsoftheladle,aseriesofimprovementmeasureshavebeenproposed,suchasoptimizingtherefractorymaterialsinvariouspartsoftheladle,layingprotectivemeasuresinkeypartsoftheladle,usinghigh-performanceandlong-lifebreathablebricks,andoptimizingtheturnoverrhythmoftheladle,etc.Thepracticalverificationwascarriedoutina120trefiningladle.Thepracticalresultsshowthatthroughtheaboveimprovementmeasures,theaverageprimaryageoftheladlehasbeenincreasedfrom42.35heatsto62.77heats,withthehighestladleagereaching72heats.Thecostofrefractorymaterialsandladleinvestmenthassignificantlydecreased,andithasgreatlypromotedthestableoperationofproductionorganization.
作者：张响 张文祥 武晓阳 姜名贞 李硕 李双武Author：ZHANGXiang ZHANGWenxiang WUXiaoyang JIANGMingzhen LIShuo LIShuangwu
作者单位：唐山钢铁集团有限责任公司,河北唐山063000
刊名：工业炉 ISTIC
Journal：IndustrialFurnace
年，卷(期)：2024, 46(3)
分类号：TQ175
关键词：精炼钢包 包龄 耐材优化 周转 生产实践
Keywords：refiningladle ladleage optimizationofrefractormaterials turnover productivepractice
机标分类号：TF811TS105.213TD952
在线出版日期：2024年6月25日
基金项目：提高120t精炼钢包一次包龄的生产实践[
期刊论文] 工业炉--2024, 46(3)张响 张文祥 武晓阳 姜名贞 李硕 李双武针对钢包一次包龄低的问题,通过对钢包各部位砖型损毁机理进行分析,提出了一系列改进措施,包括:钢包各部位耐材材质优化;钢包重点部位砌筑防护;使用高性能、长寿命透气砖;优化钢包周转节奏等,并在120t精炼钢包中进行实践...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
提高120t精炼钢包一次包龄的生产实践 Production Practice of Increasing Primary Ladle Age of 120 t Refining Ladle
提高120t精炼钢包一次包龄的生产实践.pdf
- 文件大小:
- 790.89 KB
- 下载次数:
- 60
-
高速下载
|