文档名：无铬耐指纹热镀铝锌钢板黑斑缺陷研究
摘要：采用ZEISSMerlinCompact场发射扫描电镜、OXFORDX-maxN型能谱仪、激光共聚焦显微镜等分析技术对无铬耐指纹热镀铝锌钢板黑斑缺陷进行了原因分析并提出了改进措施.结果表明:黑斑缺陷主要是由于镀层厚度凹凸不平致使钝化膜分布不均匀,镀层薄的部位钝化膜厚,镀层厚的部位钝化膜薄,钢卷在运输过程中钢板层与层之间相互摩擦致使钝化膜破损甚至脱落,导致钢板表面反射率不同,从而产生黑斑缺陷.
Abstract：ZEISSMerlinCompactfieldemissionscanningelectronmicroscope,OXFORDX-maxNenergyspectrometer,laserconfocalmicroscopeandotheranalyticaltechniqueswereusedtoanalyzethecausesofblackspotdefectofchromium-freefingerprint-resistanthot-dipaluminizedzincsteelplate.Andtheimprovementmeasureswerealsoputforward.Theresultsshowthattheblackspotdefectismainlyduetotheunevendistributionofthepassivefilmcausedbytheuneventhicknessofthecoat-ing.Thepassivefilmisthickwherethecoatingisthin,andthepassivefilmisthinwherethecoatingisthick.Duringthetransportationofthesteelcoil,thefrictionbetweenthesteelplatelayerscausesthepassivefilmtobedamagedorevendetached,resultingindifferentreflectivityofthesteelplatesurface,resultinginblackspotdefects.
作者：李积鹏 姚莹 刘小华 李健 孙朝勇 许明文 高士伟 Author：LiJipeng YaoYing LiuXiaohua LiJian SunChaoyong XuMingwen GaoShiwei
作者单位：酒钢宏兴股份有限公司碳钢薄板厂,甘肃嘉峪关735100酒钢宏兴股份有限公司钢铁研究院,甘肃嘉峪关735100
刊名：电镀与精饰
Journal：Plating&Finishing
年，卷(期)：2024, 46(2)
分类号：TG174.4
关键词：热镀铝锌 黑斑 微观形貌 钝化膜
Keywords：hot-dipaluminizedzinc blackspot micro-morphology passivefilm
机标分类号：TG174R742.1R34
在线出版日期：2024年3月1日
基金项目：甘肃省科技重大专项无铬耐指纹热镀铝锌钢板黑斑缺陷研究[
期刊论文] 电镀与精饰--2024, 46(2)李积鹏 姚莹 刘小华 李健 孙朝勇 许明文 高士伟采用ZEISSMerlinCompact场发射扫描电镜、OXFORDX-maxN型能谱仪、激光共聚焦显微镜等分析技术对无铬耐指纹热镀铝锌钢板黑斑缺陷进行了原因分析并提出了改进措施.结果表明:黑斑缺陷主要是由于镀层厚度凹凸不平致使钝化...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
无铬耐指纹热镀铝锌钢板黑斑缺陷研究 Study on black spot defect of chromium-free fingerprint-resistant hot-dip aluminized zinc steel plate
无铬耐指纹热镀铝锌钢板黑斑缺陷研究.pdf
- 文件大小:
- 1.5 MB
- 下载次数:
- 60
-
高速下载
|