摘要：采用深海高效串型试验装置对Ni-Cr-Mo-V高强钢在西太平洋深海环境中进行了深海腐蚀试验,并利用扫描电镜、能谱仪、拉曼光谱仪和扫描开尔文探针等方法,研究了该钢在500,800,1200,2000m海深下的腐蚀行为.结果表明:Ni-Cr-Mo-V高强钢在500,800,1200,2000m深海环境中暴露1a后的腐蚀速率分别为0.130,0.096,0.093,0.081mm/a,腐蚀速率随深度的增加逐渐减小;在深海环境中,该钢表面形成浅碟状点蚀坑,部分区域点蚀坑合并形成均匀腐蚀形貌;该钢在深海环境中的腐蚀产物主要包括α-Fe2O3、γ-FeOOH与α-FeOOH.
Abstract：Thedeep-seacorrosiontestofNi-Cr-Mo-Vhighstrengthsteelinthedeep-seaenvironmentoftheWesternPacificOceanwascarriedoutbyadeep-seahigh-efficiencytandemtestdevice.Thecorrosionbehaviorofthesteelat500,800,1200and2000mseadepthswasstudiedbymeansofscanningelectronmicroscopy,energydispersivespectroscopy,RamanspectroscopyandscanningKelvinprobe.TheresultsshowthatthecorrosionratesofNi-Cr-Mo-Vhigh-strengthsteelexposedto500,800,1200and2000mdeep-seaenvironmentfor1awere0.130,0.096,0.093and0.081mm/a,respectively.Thecorrosionratedecreasedwiththeincreaseofdepth.Inthedeepseaenvironment,shallowdish-likepittingpitswereformedonthesurfaceofthesteel,andpitsinsomeareasmergedtoformuniformcorrosionmorphology.Thecorrosionproductsofthesteelindeepseaenvironmentmainlyincludedα-Fe2O3,γ-FeOOHandα-FeOOH.
作者：彭文山 马力 辛永磊 丁康康 侯健Author：PENGWenshan MALi XINYonglei DINGKangkang HOUJian
作者单位：中国船舶集团有限公司第七二五研究所海洋腐蚀与防护重点实验室,青岛266237
刊名：腐蚀与防护 ISTICPKU
Journal：CorrosionandProtection
年，卷(期)：2024, 45(6)
分类号：TG172
关键词：深海环境 Ni-Cr-Mo-V高强钢 腐蚀 实海试验
Keywords：deepseaenvironment Ni-Cr-Mo-Vhighstrengthsteel corrosion realseaexperiment
机标分类号：TG172.5TE98O646.6
在线出版日期：2024年7月18日
基金项目：西太平洋深海环境中Ni-Cr-Mo-V高强钢的腐蚀行为[
期刊论文] 腐蚀与防护--2024, 45(6)彭文山 马力 辛永磊 丁康康 侯健采用深海高效串型试验装置对Ni-Cr-Mo-V高强钢在西太平洋深海环境中进行了深海腐蚀试验,并利用扫描电镜、能谱仪、拉曼光谱仪和扫描开尔文探针等方法,研究了该钢在500,800,1200,2000m海深下的腐蚀行为.结果表明:Ni-Cr-M...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
西太平洋深海环境中Ni-Cr-Mo-V高强钢的腐蚀行为 Corrosion Behavior of Ni-Cr-Mo-V High Strength Steel in Deep Sea Environment of Western Pacific Ocean
西太平洋深海环境中Ni-Cr-Mo-V高强钢的腐蚀行为.pdf
- 文件大小:
- 5.54 MB
- 下载次数:
- 60
-
高速下载
|
|