摘要：通过电化学测试和FeCl3点蚀试验,研究了Cr23C6析出相及Al2O3夹杂物对L80-9Cr钢耐蚀性的影响.结果表明:Cr23C6在原马氏体板条束内的析出聚集增大了小角度晶界处的晶格畸变程度,使其具有较高的电化学活性,导致材料耐腐蚀性能降低;另一方面,Cr23C6析出导致周围贫Cr区的形成,增大材料的点蚀倾向;此外,Al2O3夹杂物的存在也为点蚀萌生与发展提供有利位置,两者的共同作用导致L80-9Cr钢的严重点蚀.
Abstract：TheeffectsofCr23C6precipitatesandAl2O3inclusionsonthecorrosionresistanceofL80-9CrsteelwerestudiedbyelectrochemicaltestandFeCl3pittingtest.TheresultsshowthattheprecipitationandaggregationofCr23C6intheoriginalmartensiticlathbundlesincreasedthedegreeoflatticedistortionatthesmall-anglegrainboundaries,makingithavehigherelectrochemicalactivityandreducingthecorrosionresistanceofthematerial.Ontheotherhand,theprecipitationofCr23C6ledtotheformationofthesurroundingCr-depletedarea,whichincreasedthetendencyofpittingcorrosionofthematerial.Inaddition,theexistenceofAl2O3inclusionsalsoprovidedafavorablepositionfortheinitiationanddevelopmentofpittingcorrosion,andthecombinedeffectofthetwoledtotheseverepittingcorrosionofL80-9Crsteel.
作者：卢道胜 陈宇凡 魏安超 董社霞 刘勇 杜宇峰 孙冲 Author：LUDaosheng CHENYufan WEIAnchao DONGShexia LIUYong DUYufeng SUNChong
作者单位：中海油田服务股份有限公司天津分公司,天津300451中国石油大学(华东)材料科学与工程学院,青岛266580中海油田服务股份有限公司海南分公司,海口570312
刊名：腐蚀与防护 ISTICPKU
Journal：CorrosionandProtection
年，卷(期)：2024, 45(6)
分类号：TG178
关键词：L80-9Cr钢 Al2O3夹杂 富Cr碳化物 FeCl3点蚀 晶格畸变
Keywords：L80-9Crsteel Al2O3inclusion Cr-richcarbide FeCl3pittingcorrosion latticedistortion
机标分类号：TG156.5O646.54TU473
在线出版日期：2024年7月18日
基金项目：中国海油石油集团有限公司-关键技术攻关项目，中央高校基本科研业务费专项资金项目析出相及夹杂物对L80-9Cr钢耐蚀性的影响[
期刊论文] 腐蚀与防护--2024, 45(6)卢道胜 陈宇凡 魏安超 董社霞 刘勇 杜宇峰 孙冲通过电化学测试和FeCl3点蚀试验,研究了Cr23C6析出相及Al2O3夹杂物对L80-9Cr钢耐蚀性的影响.结果表明:Cr23C6在原马氏体板条束内的析出聚集增大了小角度晶界处的晶格畸变程度,使其具有较高的电化学活性,导致材料耐腐...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
析出相及夹杂物对L80-9Cr钢耐蚀性的影响 Effects of Precipitates and Inclusions on Corrosion Resistance of L80-9Cr Steel
析出相及夹杂物对L80-9Cr钢耐蚀性的影响.pdf
- 文件大小:
- 5.67 MB
- 下载次数:
- 60
-
高速下载
|
|