文档摘要：负极集流体是锂离子电池的重要组成部分,直接决定电池的内阻,影响电池的倍率和循环稳定性.以常规铜箔和多孔铜箔作为集流体制备锂离子电池,通过SEM、极片电阻、接触角和恒流充放电等测试,研究铜箔带孔对电池容量、倍率性能及循环性能的影响.与常规铜箔相比,以多孔铜箔作为集流体制备的极片具有更低的电阻率和更佳的电解液浸润效果,制备的扣式半电池以0.1C在0.001～2.500V循环3次进行化成后,首次充放电比容量分别提高了149.50mAh/g和207.03mAh/g;在10.0C倍率下的平均放电比容量达127.21mAh/g,较常规铜箔制备的电池提升了46.28%;以1.0C在0.001～2.500V循环200次后,电池的容量保持率达52.85%,材料的倍率性能和循环稳定性得到提升.
Abstract：TheanodecollectorisanimportantpartofLi-ionbattery,whichdirectlydeterminestheinternalresistanceofthebatteryandaffectstherateandcyclestabilityofthebattery.Li-ionbatterieswithconventionalcopperfoilandporouscopperfoilasthecollectorareprepared,andtheeffectsofcopperfoilwithholesonthebatterycapacity,ratecapabilityandcycleperformanceareinvestigatedbySEM,electroderesistivity,contactangleandgalvanostaticcharge-dischargetests.Comparedwiththeconventionalcopperfoil,theelectrodepreparedwithporouscopperfoilasthecollectorhaslowerresistivityandbetterelectrolytewettingeffect.Afterbeingformattedbycycling3timesat0.1Cin0.001-2.500V,theinitialcharge-dischargespecificcapacityofthepreparedhalfbatteryisincreasedby149.50mAh/gand207.03mAh/g,respectively.Theaveragespecificdischargecapacityreaches127.21mAh/gatarateof10.0C,improving46.28%comparedtothebatterypreparedwithconventionalcopperfoil.After200cyclesin0.001-2.500Vat1.0C,thecapacityretentionrateofthebatteryis52.85%,therateandcyclestabilityofthematerialareimproved.
作者：田文燕 班宵汉 刘富亮 陈晓涛 石斌Author：TIANWenyan BANXiaohan LIUFuliang CHENXiaotao SHIBin
作者单位：贵州梅岭电源有限公司,特种化学电源全国重点实验室,贵州遵义563003
刊名：电池 ISTICPKU
Journal：BatteryBimonthly
年，卷(期)：2024, 54(3)
分类号：TM912.9
关键词：锂离子电池 多孔铜箔 硬碳 容量 循环性能
Keywords：Li-ionbattery porouscopperfoil hardcarbon capacity cycleperformance
机标分类号：TM912.9TM53TM242
在线出版日期：2024年7月17日
基金项目：贵州省科技计划项目多孔铜箔对硬碳负极电化学性能的影响[
期刊论文] 电池--2024, 54(3)田文燕 班宵汉 刘富亮 陈晓涛 石斌负极集流体是锂离子电池的重要组成部分,直接决定电池的内阻,影响电池的倍率和循环稳定性.以常规铜箔和多孔铜箔作为集流体制备锂离子电池,通过SEM、极片电阻、接触角和恒流充放电等测试,研究铜箔带孔对电池容量、倍率性能...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
关键词：锂离子电池,多孔铜箔,硬碳,容量,循环性能,
- 文件大小:
- 8.45 MB
- 下载次数:
- 60
-
高速下载
|
|
1