GH625镍基高温合金化学抛光工艺
文档名：GH625镍基高温合金化学抛光工艺
摘要：[目的]化学抛光是高温合金化学铣切的关键步骤之一,能够去除高温合金表面的微观不平整缺陷,令其满足航空航天、石油化工等领域对零件表面高品质的要求.[方法]通过正交试验和单因素实验研究了抛光液配方和工艺参数对GH625高温合金化学抛光速率和表面粗糙度的影响.[结果]GH625高温合金化学抛光的较佳配方和工艺条件为:盐酸100g/L,硝酸170g/L,氢氟酸90g/L,Fe3+170g/L,温度50℃,时间5min,试片水平放置.在该条件下化学抛光后,GH625高温合金表面变得平整均匀而富有金属光泽,表面粗糙度Ra从初始的10.3μm降至1.1μm.[结论]本文的研究结果可为GH625高温合金的化学抛光提供参考.
Abstract：Chemicalpolishingisoneofthekeystepsinchemicalmillingofsuperalloys,whichcanremovemicroscopicallyunevendefectsontheirsurfaces,enablingthesuperalloystomeetthehigh-qualitysurfacerequirementsofaerospace,petrochemical,andotherfields.TheeffectsofthecompositionofpolishingsolutionandprocessparametersonthematerialremovalrateandsurfaceroughnessofGH625superalloywerestudiedbyorthogonaltestandsingle-factorexperiments.ThecompositionofpolishingsolutionandprocessparametersforchemicalpolishingofGH625superalloywereoptimizedasfollows:chlorideacid100g/L,nitricacid170g/L,hydrofluoricacid90g/L,Fe3+170g/L,temperature50℃,time5min,andhorizontalplacementofspecimensinpolishingsolution.Afterbeingchemicallypolishedundertheoptimizedconditions,thesurfaceofGH625superalloybecamesmooth,uniform,andbright,anditssurfaceroughnessRawasdecreasedfrom10.3μminitiallyto1.1μm.ThisresearchprovidesareferenceforchemicalpolishingofGH625superalloy.
作者：马宁张峻山Author：MANingZHANGJunshan
作者单位：沈阳航空航天大学机电工程学院,辽宁沈阳110136
刊名：电镀与涂饰
Journal：Electroplating&Finishing
年，卷(期)：2024, 43(4)
分类号：TG175
关键词：镍基高温合金化学抛光表面粗糙度材料去除速率
Keywords：nickel-basedsuperalloychemicalpolishingsurfaceroughnessmaterialremovalrate
机标分类号：TG132.3TG407TG506
在线出版日期：2024年5月11日
基金项目：GH625镍基高温合金化学抛光工艺[
期刊论文]电镀与涂饰--2024, 43(4)马宁张峻山[目的]化学抛光是高温合金化学铣切的关键步骤之一,能够去除高温合金表面的微观不平整缺陷,令其满足航空航天、石油化工等领域对零件表面高品质的要求.[方法]通过正交试验和单因素实验研究了抛光液配方和工艺参数对GH625...参考文献和引证文献