镀钛对2195铝锂合金耐磨和腐蚀性能的影响
文档名：镀钛对2195铝锂合金耐磨和腐蚀性能的影响
摘要：通过摩擦磨损试验和电化学工作站等测试,研究了2195-T6铝锂合金表面镀钛处理前后的摩擦磨损性能和电化学性能,探讨了浸泡实验的腐蚀机制.结果表明:镀钛后铝锂合金表层的纳米压痕硬度略有提高,表层晶粒得到了细化;镀钛前后的摩擦系数基本相同,磨损性能得到了提高;镀钛后铝锂合金的腐蚀电位提高,腐蚀电流密度减小,阻抗谱半径变大.3.5%NaCl溶液中的浸泡实验显示,镀钛试样的点腐蚀明显改善,这是由于合金表面形成的钛膜起到了隔离保护作用.
Abstract：Thewearandelectrochemicalpropertiesof2195-T6Al-Lialloybeforeandaftertitaniumplatingwereinvestigatedbyfriction-weartestandelectrochemicalmeasurement,respectively.Thecorrosionmechanismofimmersionexperimentwasdiscussed.TheresultsindicatethatthesurfacenanoindentationhardnessofAl-Lialloyslightlyincreasesandthesurfacegrainsarerefinedaftertitani-umplating.Thefrictioncoefficientsarebasicallythesamebeforeandaftertitaniumplating,andthewearperformanceisimproved.ThecorrosionpotentialofAl-Lialloyincreases,thecorrosioncurrentdensityreduces,andtheimpedancespectrumradiusenlargesaftertitaniumplating.Thisisbecausethetitaniumfilmformedonthealloyplaystherolesofisolationandprotection.
作者：苏海 张殿喜 窦忠宇 陈召松 吴明华 Author：SuHai ZhangDianxi DouZhongyu ChenZhaosong WuMinghua
作者单位：安顺学院电子与信息工程学院,贵州安顺561000;贵州安大航空锻造有限责任公司,贵州安顺561000安顺学院电子与信息工程学院,贵州安顺561000
刊名：电镀与精饰 ISTICPKU
Journal：Plating&Finishing
年，卷(期)：2024, 46(5)
分类号：TG174
关键词：铝锂合金镀钛摩擦磨损腐蚀性能
Keywords：aluminumlithiumalloyplatingtitaniumfrictionandwearcorrosionperformance
机标分类号：TG146.2TG453TG249
在线出版日期：2024年5月16日
基金项目：合作协同育人项目镀钛对2195铝锂合金耐磨和腐蚀性能的影响[
期刊论文]电镀与精饰--2024, 46(5)苏海张殿喜窦忠宇陈召松吴明华通过摩擦磨损试验和电化学工作站等测试,研究了2195-T6铝锂合金表面镀钛处理前后的摩擦磨损性能和电化学性能,探讨了浸泡实验的腐蚀机制.结果表明:镀钛后铝锂合金表层的纳米压痕硬度略有提高,表层晶粒得到了细化;镀钛前...参考文献和引证文献