LiMn0.75Fe0.25PO4基混合正极材料性能调控研究
文档名：LiMn0.75Fe0.25PO4基混合正极材料性能调控研究
摘要：重安全、降成本是未来锂电池发展的趋势.为了兼顾磷酸锰铁锂的高安全性能和三元正极材料的高比容量,采用物理混合法将磷酸锰铁锂(LMFP)与三元正极材料(NCM)进行混合,探究了不同混合量和充放电区间对混合正极材料电化学性能的影响.优化结果表明,掺入NCM后,电压跳水现象得到抑制,掺杂量为30%时,在25℃室温、2.0～4.4V、1C条件下循环200次,剩余比容量131.8mAh/g,容量保持率为96.3%.同时,穿刺实验中看不到明显的火花现象.
Abstract：Safety-orientedandcost-reducingarethefuturedevelopmenttrendoflithiumbattery.Inordertotakeintoaccountthehighsafetyoflithiummanganeseironphosphate(LMFP)andthehighspecificcapacityoftheternarycathodematerial(NCM),thephysicalmixingmethodwasusedtomixsuchtwoactivematerialsintomixedcathodematerials,andtestifytheeffectofdifferentmixingamountsandchargedischargeintervalsontheelectrochemicalperformanceofmixedcathodemateri-als.Theoptimizedresultsshowedthatthevoltagedivingphenomenonwassuppressedaftertheaddi-tionofNCM.Whenthemixedamountwas30%ofNCM,theremaining131.8mAh/gwasleftafter200cyclesundertheconditionsof25℃roomtemperature,2.0～4.4Vand1C,andthecapacityreten-tionratewas96.3%.Therewasnoobvioussparkphenomenoninthepuncturetest.
作者：蔺成良 赵美菊 袁云泉 金永成 Author：LINChengliang ZHAOMeiju YUANYunquan JINYongcheng
作者单位：中国海洋大学材料科学与工程学院,山东青岛266000山东天瀚新能源科技有限公司,山东枣庄277800
刊名：电源技术
Journal：ChineseJournalofPowerSources
年，卷(期)：2024, 48(1)
分类号：TM912
关键词：磷酸锰铁锂三元正极材料放电区间高温
Keywords：lithiummanganeseironphosphateternarycathodematerialdischargeintervalshightemperature
机标分类号：TM912.9TB383TM242:TM205.1
在线出版日期：2024年3月5日
基金项目：LiMn0.75Fe0.25PO4基混合正极材料性能调控研究[
期刊论文]电源技术--2024, 48(1)蔺成良赵美菊袁云泉金永成重安全、降成本是未来锂电池发展的趋势.为了兼顾磷酸锰铁锂的高安全性能和三元正极材料的高比容量,采用物理混合法将磷酸锰铁锂(LMFP)与三元正极材料(NCM)进行混合,探究了不同混合量和充放电区间对混合正极材料电化学性...参考文献和引证文献