316H不锈钢母材与焊缝在模拟沿海大气中的高温腐蚀行为
文档名：316H不锈钢母材与焊缝在模拟沿海大气中的高温腐蚀行为
摘要：采用高温腐蚀试验,研究了316H不锈钢母材与焊缝在520℃模拟沿海大气环境中长达3000h的高温腐蚀行为.采用扫描电镜、能谱仪和X射线衍射仪对腐蚀产物形貌和成分进行了观察和分析,并探讨了其腐蚀机理.结果表明:焊缝与母材的腐蚀质量增加曲线均符合抛物线规律;高温腐蚀3000h后,母材和焊缝试样的腐蚀均轻微,氧化层致密且无剥落,主要成分为(Cr,Fe)2O3,其腐蚀速率分别为0.44,0.61μm/a,均小于0.001mm/a,均属于完全耐蚀级别;焊缝试样的腐蚀速率略大于母材,原因是母材中的Cr与Mo含量较高.
Abstract：Thehightemperaturecorrosionbehaviorof316Hstainlesssteelbasemetalandweldinsimulatedcoastalatmosphericenvironmentwasstudiedbyhightemperaturecorrosiontestat520℃for3000h.Themorphologyandcompositionofcorrosionproductswereobservedandanalyzedbyscanningelectronmicroscopy,energydispersivespectrometerandX-raydiffractometer.Thecorrosionmechanismwasdiscussed.Theresultsshowthatthecorrosionmassincreasecurvesoftheweldandbasemetalconformedtotheparaboliclaw.After3000hofhightemperaturecorrosion,thecorrosionofbasemetalandweldsampleswasslight,andtheoxidelayerwasdenseandwithoutspalling.Themaincomponentwas(Cr,Fe)2O3,andthecorrosionrateswere0.44and0.61μm/a,respectively,bothofwhichwerelessthan0.001mm/a,allofwhichbelongedtothecompletecorrosionresistancelevel.ThecorrosionrateoftheweldsamplewasslightlyhigherthanthatofthebasemetalbecauseofthehighercontentofCrandMointhebasemetal.
作者：孟令奇 柳志浩 夏侯俊招 顾佳磊 刘光明 师超 Author：MENGLingqi LIUZhihao XIAHOUJunzhao GUJialei LIUGuangming SHIChao
作者单位：上海电气核电设备有限公司,上海201306南昌航空大学材料科学与工程学院,南昌330063
刊名：腐蚀与防护 ISTICPKU
Journal：CorrosionandProtection
年，卷(期)：2024, 45(6)
分类号：TG174
关键词：316H不锈钢焊缝母材模拟沿海大气高温腐蚀
Keywords：316Hstainlesssteelweldbasemetalsimulatedcoastalatmospherehightemperaturecorrosion
机标分类号：TG172.3U452.12TE988.2
在线出版日期：2024年7月18日
基金项目：316H不锈钢母材与焊缝在模拟沿海大气中的高温腐蚀行为[
期刊论文]腐蚀与防护--2024, 45(6)孟令奇柳志浩夏侯俊招顾佳磊刘光明师超采用高温腐蚀试验,研究了316H不锈钢母材与焊缝在520℃模拟沿海大气环境中长达3000h的高温腐蚀行为.采用扫描电镜、能谱仪和X射线衍射仪对腐蚀产物形貌和成分进行了观察和分析,并探讨了其腐蚀机理.结果表明:焊缝与母材...参考文献和引证文献