包覆低共熔溶剂的聚苯乙烯微胶囊吸附Li 的性能研究
文档名：包覆低共熔溶剂的聚苯乙烯微胶囊吸附Li 的性能研究
摘要：为实现绿色、低成本从海水中提锂的目标,采用同轴共流微流体技术结合溶剂挥发法制备包覆有低共熔溶剂(甲基三辛基氯化铵/癸酸)的聚苯乙烯微胶囊.所制备的微胶囊颗粒呈均一的球形.将该微胶囊用作萃取Li+吸附剂,系统研究了吸附时间、吸附温度、溶液pH、初始锂浓度和固液比对Li+吸附量和萃取率的影响.结果表明在吸附Li+水溶液时,微胶囊对Li+的最大吸附量为32mg·g-1.碱性条件时微胶囊对模拟海水中的Li+吸附分配比为10.22L·g-1.
Abstract：Toachieveenvironmentfriendlyandlow-costlithiumextractionfromseawater,aco-axialmicrofluidictechnologycombinedwithasolventevaporationmethodwasemployedtopreparepolystyrenemicrocapsulescoatingadeepeutecticsolvent(methyltrioctylammoniumchloride/decanoicacid).Theresultingmicrocapsulesexhibitsuniformsphericalmorphology.ThesemicrocapsuleswereemployedasLi+adsorbents,andasystematicinvestigationwasconductedtostudytheeffectsofadsorptiontime,temperature,solutionpH,initialLi+concentration,andsolid-liquidratioonLi+adsorptioncapacityandextractionefficiency.TheresultsdemonstrateamaximumLi+adsorptioncapacityof32mg·g-1whenadsorbingLi+fromaqueoussolutions.Furthermore,thedistributionratioofLi+fromsimulatedseawaterbymicrocapsulesis10.22L·g-1underalkalineconditions.
作者：侯晓静王彦旭吴可君何潮洪Author：HOUXiaojingWANGYanxuWUKejunHEChaohong
作者单位：浙江大学化学工程与生物工程学院浙江省化工高效制造技术重点实验室,浙江杭州310058;浙江大学衢州研究院,浙江衢州324000
刊名：高校化学工程学报 ISTICEIPKU
Journal：JournalofChemicalEngineeringofChineseUniversities
年，卷(期)：2024, 38(3)
分类号：TQ028.8
关键词：微胶囊提锂低共熔溶剂溶剂挥发法吸附
Keywords：microcapsuleextractinglithiumdeepeutecticsolventsolventevaporationmethodadsorption
机标分类号：TQ423O65R683.4
在线出版日期：2024年7月8日
基金项目：国家自然科学基金包覆低共熔溶剂的聚苯乙烯微胶囊吸附Li+的性能研究[
期刊论文]高校化学工程学报--2024, 38(3)侯晓静王彦旭吴可君何潮洪为实现绿色、低成本从海水中提锂的目标,采用同轴共流微流体技术结合溶剂挥发法制备包覆有低共熔溶剂(甲基三辛基氯化铵/癸酸)的聚苯乙烯微胶囊.所制备的微胶囊颗粒呈均一的球形.将该微胶囊用作萃取Li+吸附剂,系统研究了...参考文献和引证文献