摘要：GH4169高温合金常温和高温条件下硬度及强度较高,常规金属切削的热软化效应不明显,同时由于材料热导率低,加工硬化明显,采用传统数控加工方式存在刀具易磨损、加工效率低等问题.为实现高温合金的优质高效加工,开展不同加工工艺参数下的常规铣削及超声铣削力学响应对比实验,分析同一工况下常规铣削和超声辅助铣削的刀具磨损,揭示了不同加工参数对铣削力的影响规律及侧铣过程中超声辅助铣削较常规铣削的优势.
Abstract：GH4169high-temperaturealloyhasextremelyhighhardnessandstrengthundernormalandhightemper-atureconditions.Thethermalsofteningeffectofconventionalmetalcuttingisnotobvious.Atthesametime,duetothelowthermalconductivityandobviousworkhardeningofthematerial,traditionalCNCmachiningmethodshaveproblemssuchastoolwearandlowmachiningefficiency.Therefore,inordertoachievehigh-qualityandefficientprocessingofhigh-tem-peraturealloys.Comparativeexperimentsareconductedonthemechanicalresponseofconventionalmillingandultrasonictestingunderdifferentprocessingparameters,andthetoolwearexperimentsofconventionalmillingandultrasonicassistedmillingunderthesameworkingconditionareanalyzed.Theinfluenceofdifferentprocessingparametersonmillingforceandtheadvantagesofultrasonicassistedmillingoverconventionalmillinginthesidemillingprocessarerevealed.
作者：袁盛旺周何情Author：YuanShengwangZhouHeqing
作者单位：中国航发成都发动机有限公司
刊名：工具技术 ISTICPKU
Journal：ToolEngineering
年，卷(期)：2024, 58(6)
分类号：TG713TH162
关键词：GH4169高温合金超声辅助切削刀具磨损力学响应
Keywords：GH4169high-temperaturealloyultrasonicassistedtoolwearmechanicalresponse
机标分类号：TG115.6+3TG506.5TH161
在线出版日期：2024年6月25日
基金项目：GH4169高温合金超声辅助切削试验研究[
期刊论文]工具技术--2024, 58(6)袁盛旺周何情GH4169高温合金常温和高温条件下硬度及强度较高,常规金属切削的热软化效应不明显,同时由于材料热导率低,加工硬化明显,采用传统数控加工方式存在刀具易磨损、加工效率低等问题.为实现高温合金的优质高效加工,开展不同加...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
GH4169高温合金超声辅助切削试验研究Experimental Study on Optimization of Ultrasonic Assisted Process Parameters for GH4169 Alloy
GH4169高温合金超声辅助切削试验研究.pdf
页:
[1]