文档名：二次锂化法制备LiNi0.931Co0.049Al0.02O2单晶正极材料
摘要：通过二次锂化技术制备了LiNi0.931Co0.049Al0.02O2单晶NCA正极材料.通过高温预烧结完成Li0.96Ni0.95Co0.05O2材料的制备;随后在预烧结后的物料中补充足够的Al和Li,进行二次烧结制备出NCA单晶正极材料(S2-NCA).通过本技术制备的高镍单晶正极材料表现出了优异的倍率和循环性能.经过测试,S2-NCA放电比容量可达217.1mAh/g,60次循环容量保持率可达94.8%,远远优于一次锂化制备的NCA单晶正极材料(S1-NCA),初始比容量为207.9mAh/g,60次循环容量保持率为85.8%.
Abstract：Singlecrystalcathodematerial(LiNi0.931Co0.049Al0.02O2)waspreparedbysecondarylithiationtechnology.Firstly,Li0.96Ni0.95Co0.05O2waspreparedthroughhightemperaturepre-sintering.Then,AlandLiwereaddedintothepre-sinteringmaterial,andNCAsinglecrystalcathodematerial(S2-NCA)waspreparedbysecondarysintering.Thehighnickelsinglecrystalcathodematerialpreparedbythistechnologyshowsexcellentmagnificationandcyclingperformance.Thefirstdischargespe-cificcapacityofS2-NCAis217.1mAh/g,andthecyclecapacityretentionrateafter60cyclesis94.8%,whenthoseare207.9mAh/gand85.8%ofS1-NCA.
作者：李文升 马帅 罗广求 郑见杰 Author：LIWensheng MAShuai LUOGuangqiu ZHENGJianjie
作者单位：天津蓝天太阳科技有限公司,天津300384;中国电子科技集团公司第十八研究所,天津300384天津蓝天太阳科技有限公司,天津300384中国电子科技集团公司第十八研究所,天津300384
刊名：电源技术
Journal：ChineseJournalofPowerSources
年，卷(期)：2024, 48(1)
分类号：TM912
关键词：二次锂化法单晶正极材料电性能
Keywords：secondarylithiationprocesssinglecrystalcathodematerialselectricalperformance
机标分类号：TB321TM912.9TM242
在线出版日期：2024年3月5日
基金项目：二次锂化法制备LiNi0.931Co0.049Al0.02O2单晶正极材料[
期刊论文]电源技术--2024, 48(1)李文升马帅罗广求郑见杰通过二次锂化技术制备了LiNi0.931Co0.049Al0.02O2单晶NCA正极材料.通过高温预烧结完成Li0.96Ni0.95Co0.05O2材料的制备;随后在预烧结后的物料中补充足够的Al和Li,进行二次烧结制备出NCA单晶正极材料(S2-NCA).通过本技...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
二次锂化法制备LiNi0.931Co0.049Al0.02O2单晶正极材料Preparation of single crystal LiNi0.931Co0.049Al0.02O2 cathode via second-ary lithiation process
二次锂化法制备LiNi0.931Co0.049Al0.02O2单晶正极材料.pdf
页:
[1]