二次铝灰基多孔莫来石陶瓷制备研究
文档名：二次铝灰基多孔莫来石陶瓷制备研究
摘要：二次铝灰富含大量的铝元素,可在制备莫来石陶瓷材料中作为铝源.为综合利用二次铝灰,将水洗焙烧后的二次铝灰、活性硅粉、玉米淀粉和聚乙烯醇(PVA)结合剂采用固相烧结法制备多孔莫来石陶瓷,探讨Al2O3与SiO2摩尔比、烧成温度、保温时间对试样性能的影响,并进行X射线衍射(XRD)与扫描电镜(SEM)分析.结果表明,在Al2O3与SiO2摩尔比为1.8,温度为1200℃,保温时间为4h的条件下,制备的多孔莫来石陶瓷体积密度为1.83g/cm3,吸水率为18.05%,显气孔率为32.94%,抗压强度为18.46MPa,且有柱状莫来石晶体生成,试样综合性能较优.
Abstract：Secondaryaluminiumashisrichinaluminiumandcanbeusedasanaluminiumsourceinthepreparationofmulliteceramicmateri-als.Inordertomakecomprehensiveuseofthesecondaryaluminiumash,theporousmulliteceramicswerepreparedbysolid-phasesinteringwiththesecondaryaluminiumashafterwashingandroasting,activatedsilicapowder,cornstarchandPVAbindingagent,theeffectsofthemolarratioofAl2O3toSiO2,sinteringtemperature,andholdingtimeonthepropertiesofthespecimenswereinvestigatedandanalysedbyXRDandSEM.Theresultsshowthattheporousmulliteceramicswithbulkdensityof1.83g/cm3,waterabsorptionof18.05%,apparentporosityof32.94%,compressivestrengthof18.46MPaareprepared,andcolumnarmullitecrystalsareproducedundertheconditionsofAl2O3toSiO2molarratioof1.8,temperatureof1200℃,andholdingtimeof4h,thecomprehensiveperformanceofthesampleisbetter.
作者：齐涛刘璇满苏醇刘锦川包文昊Author：QiTaoLiuXuanManSuchunLiuJinchuanBaoWenhao
作者单位：安徽工业大学冶金工程学院,安徽马鞍山243002
刊名：非金属矿 ISTIC
Journal：Non-MetallicMines
年，卷(期)：2024, 47(3)
分类号：TQ174
关键词：二次铝灰活性硅粉莫来石多孔陶瓷
Keywords：secondaryaluminiumashactivatedsilicapowdermulliteporousceramics
机标分类号：TQ174.1TQ325.9TG161
在线出版日期：2024年6月7日
基金项目：安徽工业大学高层次人才引进启动项目二次铝灰基多孔莫来石陶瓷制备研究[
期刊论文]非金属矿--2024, 47(3)齐涛刘璇满苏醇刘锦川包文昊二次铝灰富含大量的铝元素,可在制备莫来石陶瓷材料中作为铝源.为综合利用二次铝灰,将水洗焙烧后的二次铝灰、活性硅粉、玉米淀粉和聚乙烯醇(PVA)结合剂采用固相烧结法制备多孔莫来石陶瓷,探讨Al2O3与SiO2摩尔比、烧成温...参考文献和引证文献