低温热处理对聚苯胺微观结构及电化学性能的影响研究
文档名：低温热处理对聚苯胺微观结构及电化学性能的影响研究
摘要：采用电化学循环伏安法,通过改变聚合条件,在碳布上可控沉积了少量的聚苯胺.在不破坏聚苯胺分子链结构的基础上,对其进行了低温热处理,并对热处理前后的聚苯胺微观结构及电化学性能进行了表征和测试.结果表明,低温热处理可以显著改变聚苯胺的微观形貌,使聚苯胺分子链均匀铺展,团聚现象明显减少.经过200℃低温热处理后的聚苯胺其电化学性能有了明显改善,获得了更大的比容量、更高的倍率性能和更长的循环寿命.在1.0A/g的电流密度下,比电容为207.58F/g,经1000次循环后容量保持率相较于低温热处理前提高了18.06％.
Abstract：Electrochemicalcyclicvoltammetrywasusedtocontrollablydepositasmallamountofpolyanilineonthecarbonclothbychangingthepolymerizationconditions.Onthebasisofnotde-stroyingthemolecularchainstructureofpolyaniline,thelowtemperatureheattreatmentwascarriedout,andthemicrostructureandelectrochemicalpropertiesbeforeandafterheattreatmentweretestedandevaluated.Itisfoundoutthatthemicrostructureofpolyanilinecanbesignificantlychangedbylowtemperatureheattreatment,andthemolecularchainsofpolyanilinecanbeevenlyspreadwithsignificantlyreducedagglomerationphenomenon.Afterheattreatmentat200℃,theelectrochemicalperformanceofpolyanilinehasbeensignificantlyimproved,harvestinglargerspe-cificcapacitance,higherrateperformanceandlongercyclelife.Underthecurrentdensityof1.0A/g,thespecificcapacitanceis207.58F/g.After1000cycles,thecapacityretentionrateisincreasedby18.06％comparedwiththatbeforelowtemperatureheattreatment.
作者：万凯初蕾朱志斌王玮Author：WANKaiCHULeiZHUZhibinWANGWei
作者单位：中国海洋大学材料科学与工程学院,山东青岛266404
刊名：电源技术 ISTICPKU
Journal：ChineseJournalofPowerSources
年，卷(期)：2024, 48(4)
分类号：TM53
关键词：聚苯胺低温热处理微观结构电化学性能
Keywords：polyanilinelowtemperatureheattreatmentmicrostructureelectrochemicalperformance
机标分类号：O642TM912.9TQ127.1
在线出版日期：2024年6月11日
基金项目：国家自然科学基金，国家自然科学基金低温热处理对聚苯胺微观结构及电化学性能的影响研究[
期刊论文]电源技术--2024, 48(4)万凯初蕾朱志斌王玮采用电化学循环伏安法,通过改变聚合条件,在碳布上可控沉积了少量的聚苯胺.在不破坏聚苯胺分子链结构的基础上,对其进行了低温热处理,并对热处理前后的聚苯胺微观结构及电化学性能进行了表征和测试.结果表明,低温热处理...参考文献和引证文献