电解辅助磁力研磨整体叶盘试验研究
文档名：电解辅助磁力研磨整体叶盘试验研究
摘要：针对航空发动机整体叶盘结构复杂和材料难以加工的特性,在磁力研磨技术的基础上引入电解作用作为辅助手段.通过电解作用产生易于处理的钝化膜,然后再引入磁力研磨加工技术,加快了对叶盘表面纹理的去除,同时使表面加工质量更加均匀.通过3D超景深电镜观测叶盘表面形貌,结果显示:经复合研磨20min,叶盘表面纹理基本去除,表面更加细密、均匀.表面粗糙度值Ra由1.5μm降至0.4μm.
Abstract：Inviewofthecharacteristicsofaeroengineblisksuchascomplicatedstructureanddifficulttoprocessing,electrolysiswasintroducedasanauxiliarymethodonthebasisofmagneticabrasivefin-ishing(MAF)technology.Byelectrolyzingtoproduceapassivationfilmwhichwaseasytohandle,andthenMAFtechnologywasintroduced.Asaresult,theremovalofthesurfacetextureofthebliskwasac-celerated,whilewhichmadethesurfaceprocessingqualitymoreeven.Thesurfacetopographyofthebliskwasobservedby3Dsuperdepthoffieldelectronmicroscope,andtheresultsshowedthataftercompoundprocessingof20min,thesurfacetextureofthebliskwascompletelyremovedandthesur-facequalitybecamemorefineandeven.ThesurfaceroughnessvalueRawasreducedfrom1.5μmto0.4μm.
作者：于克强 周锟 靳铁辉 陈燕 Author：YuKeqiang ZhouKun JinTiehui ChenYan
作者单位：辽宁科技大学机械工程与自动化学院,辽宁鞍山114051鞍钢股份有限公司中厚板事业部,辽宁鞍山114042
刊名：电镀与精饰 ISTICPKU
Journal：Plating&Finishing
年，卷(期)：2024, 46(4)
分类号：TH161
关键词：整体叶盘磁力研磨电解磁性磨粒
Keywords：bliskmagneticabrasivefinishingelectrolysismagneticabrasive
机标分类号：TP308U461V263.6
在线出版日期：2024年5月15日
基金项目：辽宁省教育厅项目电解辅助磁力研磨整体叶盘试验研究[
期刊论文]电镀与精饰--2024, 46(4)于克强周锟靳铁辉陈燕针对航空发动机整体叶盘结构复杂和材料难以加工的特性,在磁力研磨技术的基础上引入电解作用作为辅助手段.通过电解作用产生易于处理的钝化膜,然后再引入磁力研磨加工技术,加快了对叶盘表面纹理的去除,同时使表面加工质...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
电解辅助磁力研磨整体叶盘试验研究Experimental study on blisk by electrolysis assisted MAF
电解辅助磁力研磨整体叶盘试验研究.pdf
页:
[1]