硅橡胶聚丙烯酸酯微球增韧聚乳酸研究
文档名：硅橡胶聚丙烯酸酯微球增韧聚乳酸研究
摘要：为了改善聚乳酸的韧性,将硅橡胶-聚甲基丙烯酸甲酯粒子和聚乳酸通过熔融共混制备聚乳酸共混物,研究了硅橡胶-聚甲基丙烯酸甲酯粒子交联度、核壳比以及含量对于聚乳酸力学性能的影响.结果表明,当交联剂KH570用量为8％,核壳质量比为7:3时,聚乳酸共混物的抗冲击强度为2.88kJ/m2,拉伸强度为51.08MPa,增韧效果最佳;当硅丙粒子含量从0增加至18％时,PLA的抗冲击强度从1.37kJ/m2增加至8.67kJ/m2,增加了5.33倍;拉伸强度从74.77MPa下降至38.86MPa;断裂伸长率从2.08％增加至25.45％;弯曲强度从106.64MPa下降至72.74MPa.
Abstract：Inordertoimprovethetoughnessofpolylacticacid(PLA),PLAblendwaspreparedbymeltingblendofsiliconerubber-poly(methylmethacrylate)particlesandpolylacticacid.Theeffectsofcross-linkingdegree,core-shellratioandcontentofsiliconerubber-poly(methylmethacrylate)particlesonthemechanicalpropertiesofPLAwerestudied.Theresultsshowedthattheimpactstrengthandtensilestrengthofpolylacticacidblendwere2.88kJ/m2and51.08MParespectivelywhentheamountofcrosslinkerKH570was8％andthecore-shellmassratiowas7:3.TheimpactstrengthofPLAincreased5.33timesfrom1.37kJ/m2to8.67kJ/m2whenthecontentofsilicon-Cparticlesincreasedfrom0to18％.Tensilestrengthdecreasedfrom74.77MPato38.86MPa;Elongationatbreakincreasedfrom2.08％to25.45％;Thebendingstrengthdecreasedfrom106.64MPato72.74MPa.
作者：刘美意张镇鹏马凤国Author：LIUMei-yiZHANGZhen-pengMAFeng-guo
作者单位：青岛科技大学橡塑材料与工程教育部重点实验室/山东省橡塑材料与工程重点实验室,山东青岛266042
刊名：合成材料老化与应用 ISTIC
Journal：SyntheticMaterialsAgingandApplication
年，卷(期)：2024, 53(3)
分类号：TQ323.4
关键词：硅橡胶-聚甲基丙烯酸甲酯聚乳酸增韧
Keywords：siliconerubber-polymethylmethacrylatepolylacticacidtoughening
机标分类号：TQ325.7TQ436.3TB332
在线出版日期：2024年7月3日
基金项目：硅橡胶-聚丙烯酸酯微球增韧聚乳酸研究[
期刊论文]合成材料老化与应用--2024, 53(3)刘美意张镇鹏马凤国为了改善聚乳酸的韧性,将硅橡胶-聚甲基丙烯酸甲酯粒子和聚乳酸通过熔融共混制备聚乳酸共混物,研究了硅橡胶-聚甲基丙烯酸甲酯粒子交联度、核壳比以及含量对于聚乳酸力学性能的影响.结果表明,当交联剂KH570用量为8％,核壳...参考文献和引证文献